Viewing 1 to 30 of 222
2017-11-17
WIP Standard
J420
The scope of this SAE Information Report is to provide general information relative to the nature and use of magnetic particles for nondestructive testing. The document is not intended to provide detailed technical information, but will serve as an introduction to the theory and capabilities of magnetic particle testing, and as a guide to more extensive references.
CURRENT
2017-10-30
Standard
AMS2633D
This procedure covers ultrasonic inspection of tubular, centrifugally-cast, corrosion-resistant steel cylinders.
CURRENT
2017-10-30
Standard
AS5371A
This SAE Aerospace Standard (AS) establishes requirements for the manufacture of shim-type reference standards containing artificial flaws (notches) for use in the magnetic particle inspection process.
CURRENT
2017-09-29
Standard
AMS2647F
This specification details requirements and procedures for the detection of defects in aircraft and engine components during maintenance and overhaul operations.
2017-09-26
WIP Standard
AMS2634C
This specification covers procedures for ultrasonic inspection of thin wall metal tubing of titanium, titanium alloy, and corrosion and heat resistant steels and alloys having nominal OD over 0.1875 inch (4.762 mm) with OD to wall thickness ratio of 8 or greater and wall thickness variation not exceeding + or - 10% of nominal.

This process has been used typically for locating internal defects, such as cracks, voids, seams, and other discontinuities, which may or may not be exposed to the surface, but usage is not limited to such applications.

2017-09-26
WIP Standard
ARP2654A
To provide general instructions for accomplishing ultrasonic thickness measurements. Measurements can be made from one side of a material when access to the opposite side is restricted.
2017-09-26
WIP Standard
ARP4402A
This SAE Aerospace Recommended Practice establishes the requirements and procedures for eddy current inspection of open fastener holes in aluminum aircraft structures.
2017-09-26
WIP Standard
AS4787A
This SAE Aerospace Standard (AS) establishes minimum requirements for eddy current inspection of circular holes in nonferrous, metallic, aircraft engine hardware with fasteners removed. The inspection is intended to be performed at maintenance and overhaul facilities on engine run hardware. This standard has been typically used to inspect for service-induced surface and near surface cracks, but usage is not limited to such applications.
2017-09-26
WIP Standard
AS4792B
This SAE Aerospace Standard (AS) covers water conditioning agents used to facilitate aqueous wet-method magnetic particle inspection. Such conditioning agents, in powder or liquid form, provide suitable corrosion protection, wetting, and particle dispensability properties when mixed in water for application of magnetic particles on the surface of an object for magnetic particle inspection as described in AMS3042, AMS3044, ASTM E1444, and others. Water conditioning agents can consist of varying combinations of such components as dispersants, surfactants, corrosion inhibitors, and anti-foaming agents. Individual components may be added to the bath of a system to develop specific properties. The user is referred to the manufacturer of the conditioning agent to develop the most suitable combination of ingredients for the user’s requirements.
2017-09-26
WIP Standard
AMS2644G
This specification establishes the classification, technical requirements, tests, and test procedures for the qualification, approval, and quality verification of all materials used in the liquid penetrant methods of inspection with the exception of those excluded in the application section.
2017-09-20
WIP Standard
AMS2628B
This specification covers procedures for ultrasonic immersion inspection of premium grade wrought titanium and titanium alloy round billet 5.0 inches (127 mm) and over in nominal diameter. This inspection procedure has been used typically for locating internal defects such as cracks, voids, inclusions, and other structural discontinuities which may or may not be exposed to the surface in billets, but usage is not limited to such applications. Testing normally will be by longitudinal procedure, but shear wave procedure may be added when agreed upon by purchaser and vendor. This specification includes zoned inspection and digital data acquisition.
2017-09-11
WIP Standard
AS6171/6A
Through the use of ultra-high frequency ultrasound, typically above 10 MHz, Acoustic Microscopy (AM) non-destructively finds and characterizes physical features and latent defects (visualization of interior features in a layer by layer process) - such as material continuity and discontinuities, sub-surface flaws, cracks, voids, delaminations and porosity. AM observed features and defects can be indicators that the components were improperly handled, stored, altered or previously used. If AS6171/6 is invoked in the contract, the base document, AS6171 General Requirements shall also apply.
CURRENT
2017-07-11
Standard
AS6449C
This document establishes the requirements for a dry film lubricant AS6449 lubricant for use on breathing oxygen system and potable water system components, for a temperature range of −90 to +300 °F. This document also establishes the Non-Destructive Test (NDT) procedures and criteria for coated production parts. This document requires qualified products and product applicators.
CURRENT
2017-07-11
Standard
AMS2631E
This specification covers the procedure for ultrasonic inspection of wrought titanium and titanium alloy products 0.25 inch (6.4 mm) and over in cross-section (thickness) or diameter.
CURRENT
2017-05-18
Standard
AMSSTD2154C
The purpose of this standard is to provide uniform methods for the ultrasonic inspection of wrought metals and wrought metal products.
CURRENT
2017-02-02
Standard
J379_201702
Hardness measurements are used as a quality control check of the consistency of formulation and processing of brake linings. Gogan hardness is nondestructive (the penetrator causes shallow surface deformation.). Gogan hardness method alone does not show anything about a lining’s ability to develop friction or to resist fade when used as a friction element in brakes. The hardness and the range of hardness are peculiar to each formulation, thickness, and contour; therefore, the acceptable values and ranges must be established for each formulation and part configuration by the manufacturer.
CURRENT
2016-11-29
Standard
AMS2636A
This specification covers procedures for ultrasonic immersion inspection of premium grade wrought titanium and titanium alloy forgings. Premium grade is a term used to describe titanium alloys used for critical rotating components in turbine engines. For details, see SAE AMS2380, the specification that covers the procedures for approval of products of premium-quality titanium alloys and the controls to be exercised in producing such products.
CURRENT
2016-10-30
Standard
AS6171/6
Through the use of ultra-high frequency ultrasound, typically above 10 MHz, Acoustic Microscopy (AM) non-destructively finds and characterizes physical features and latent defects (visualization of interior features in a layer by layer process) - such as material continuity and discontinuities, sub-surface flaws, cracks, voids, delaminations and porosity. AM observed features and defects can be indicators that the components were improperly handled, stored, altered or previously used. If AS6171/6 is invoked in the contract, the base document, AS6171 General Requirements shall also apply.
CURRENT
2016-01-06
Standard
AMSI83387B
This specification covers both the material and the examination process of an inspection material in the form of a dispersion of magnetic particles in a controlled viscosity rubber base that cures at room temperature by addition of one or more curing agents. The test object is magnetized with the uncured rubber covering the area of interest. The magnetic particles then migrate to the leakage field caused by the discontinuity. As the rubber cures, discontinuity indications remain in place on the rubber. The product may be supplied in a variety of viscosities and colors.
2015-08-01
WIP Standard
ARP4462A
This recommended practice covers the procedures and method for establishing acceptance criteria when performing Barkhausen noise testing of surface-hardened steel components to detect grinding burns (metallurgical damage caused by over-heating) in bare or chromium-plated parts. Primarily for nondestructive testing of heat treated, high strength low-alloy steel parts which have been ground, in accordance with MIL-STD-866 or commercial standard, before or after chromium plating. This test method may be used as an independent test or to confirm grinding damage detected in accordance with AMS 2440 or MIL-STD-867 in bare or chromium plated components.
CURRENT
2015-05-26
Standard
AMS2641C
This specification covers two types of refined hydrocarbon compounds in the form of liquids.
HISTORICAL
2014-02-06
Standard
AMS2647E
This specification details requirements and procedures for the detection of defects in aircraft and engine components during maintenance and overhaul operations.
CURRENT
2013-12-13
Standard
AMS2649D
This specification establishes the requirements for etch inspection of steel parts to detect overheating (rehardening or overtempering) caused by abusive machining or grinding, or to detect localized discontinuous carburization.
2013-10-18
WIP Standard
AMS2632B
This specification covers the procedure for ultrasonic inspection of flat, contoured, and cylindrical products having a cross sectional-thickness of 0.02 to 0.5 inches (0.5 to 12.7 mm). This specification does not apply to inspection of composite materials.

This process has been used typically for locating and defining internal defects such as cracks, voids, laminations, and other structural discontinuities which may or may not be exposed to the surface, but usage is not limited to such applications.

CURRENT
2013-10-17
Standard
AMS2644F
This specification establishes the classification, technical requirements, tests, and test procedures for the qualification, approval, and quality verification of all materials used in the liquid penetrant methods of inspection with the exception of those excluded in the application section.
CURRENT
2013-07-11
Standard
AMS2628A
This specification covers procedures for ultrasonic immersion inspection of premium grade wrought titanium and titanium alloy round billet 5.0 inches (127 mm) and over in nominal diameter.
CURRENT
2013-03-25
Standard
AS4792A
This SAE Aerospace Standard (AS) covers water conditioning agents used to facilitate aqueous wet-method magnetic particle inspection.
HISTORICAL
2012-10-30
Standard
AMS2641B
This specification covers two types of refined hydrocarbon compounds in the form of liquids.
HISTORICAL
2012-10-10
Standard
AMSSTD2154A
The purpose of this military standard is to provide uniform methods for the ultrasonic inspection of wrought metals and wrought metal products.
HISTORICAL
2012-09-24
Standard
AMS2636
This specification covers procedures for ultrasonic immersion inspection of premium grade wrought titanium and titanium alloy forgings. Premium grade is a term used to describe titanium alloys used for critical rotating components in turbine engines. For details, see SAE AMS2380, the specification that covers the procedures for approval of products of premium-quality titanium alloys and the controls to be exercised in producing such products.